Structural Parameter Table:
| Structural | Value |
| Material Options | Ceramic plated Gold/Stainless Steel/Molybdenum |
| Rod diameter | 2-16mm |
| Rod Length | 100-300mm |
| Base | Alumina Ceramic/Machinable Glass Ceramic |
| Comprehensive accuracy | ≤3μm |
99% Alumina Ceramic Material Properties
| Type | Unit | Standard | Value |
| Color | - | - | Ivory |
| Main Characteristics | - | - | Excellent plasma corrosion resistance, high wear resistance. |
| Application Field | - | - | Semiconductor equipment components, wear-resistant and corrosion-resistant parts. |
| Density | g/cm3 | ISO18754:2003 | 3.88 |
| Water Imbibition | % | - | 0 |
| Vickers Hardness | HV | ASTM-C1327-15 | 17 |
| Bending Strength | MPa | ASTM-C1161-13 | 350 |
| Compressive Strength | MPa | GB/T8489-2006 | 2450 |
| Young's Modulus | GPa | ASTM-C1198-09 | 350 |
| Poisson's Ratio | - | ASTM-C1421-18 | 0.22 |
| Fracture Toughness | MPa·m1/2 | ASTM-C1421-18 | 4-5 |
| Linear Coefficient of Expansion (40-400°C) | x10-6/°C | ASTM-E1461-13 | 8.2 |
| Thermal Conductivity (20°C) | W/(m·k) | ASTM-E1461-13 | 25-30 |
| Specific Heat | J/(kg·k)x103 | ASTM-E1461-13 | 0.8 |
| Volume Resistivity (20°C) | Ω·cm | - | >1015 |
| Dielectric Strength | KV/mm | - | 20 |
| Dielectric Constant | - | ASTM-D2149-13 | 9.2 |
| Dielectric Loss Coefficient | x10-4 | ASTM-D2149-13 | 2 |
| Nitric Acid (HNO3) (90°C) | Weight Loss | - | <0.12 |
| Sulfuric Acid (H2SO4) (95°C) | - | <0.3 | |
| Sodium Hydroxide (NaOH) (80°C) | - | <0.9 | |
| Max Using Temperature | °C | - | 1500 |
Benefits：
- Custom Specifications
- Superior Surface Treatment Technology
- High Accuracy Installation, 3um Comprehensive Tolerance
- Consistent Process Management
- High-Purity Alumina Ceramic Collars
- High-Quality Chamber and Accessory Integration