Magnesium Stabilized Zirconia Ceramic
Magnesia Stabilized Zirconia (MSZ) Ceramic is a great refractory and insulating material due to high oxygen ion conductivity, high strength and toughness, and good thermal shock resistance. It has a clean melt at temperatures above 1900°C and above and is specially manufactured for melting superalloys and precious metals. Its superior thermal shock resistance to temperatures reaching up to 2200°C.
Advantages:
- High thermal shock resistance
- High wear-resistant and erosion-resistant
- Metal corrosion resistance in high temperature
- Excellent non-wetting characteristics
- High strength
- Long service life
- The stabilizers and grains combination can be designed according to customer's using environment.
Application Temperature:
0°C-2200℃Applicable Environment:
Air, Vacuum, or Atmosphere Protection EnvironmentApplication Field:
-
High temperature melt flow control
- Sizing nozzle, Ladle skateboard panel, Converter slag blocking slide plate and ring, etc.
-
Specialty glass manufacturing
- Large size high content of zirconia and alumina ceramics, etc.
-
Metal powder industry
- Setter plate, Gas atomizing nozzle, etc.
-
Precious metal smelting industry
- Ceramic Crucibles, etc.
-
Artificial/Laser Crystal Ceramic Temperature Field
- Rare earth composite oxide solid solution ceramic temperature field, etc.
Technical Indicators:
| Indicators | Item | Units | MSZ-H | MSZ-L | Custom |
| Main Composition | ZrO2 | % | ≥95 | ≥95 | 60-95 |
| Al2O3 | % | ≤0.2 | ≤0.2 | 0.2-20 | |
| SiO2 | % | ≤0.4 | ≤0.4 | 0.2-1 | |
| MgO | % | ≤2.9 | ≤2.9 | MgO/Y2O3 | |
| Fe2O3 | % | ≤0.1 | ≤0.1 | 0.1-0.3 | |
| TiO2 | % | ≤0.1 | ≤0.1 | 0.1-1.0 | |
| Physical | Color | - | Yellow | Yellow | Yellow/White |
| Density | g/cm3 | ≤5.2 | 5.4-5.60 | 4.6-5.6 | |
| Porosity | % | ≤18.5 | ≤8 | 1-18.5 | |
| The stabilizers, grains combination and porosity can be designed according to customer’s using environment. | |||||
By Materials
Application
Download
How to get a quote?
We will support your project with the required technical and developmental support
Inquiry
Proposal
Order
Production
Delivery